S.No. |
Particulars |
|
HITITE 60 |
1 |
Nominal Density (gms/cc) |
|
1.05 |
2 |
Tensile Strength (kg/cm²) |
(Minimum) |
125 |
3 |
Compressibility at 1000 psi (%) |
|
17-30 |
4 |
Recovery (%) |
(Minimum) |
40 |
5 |
After immersion in ASTM Oil No. 3 for 22 Hrs. @ 21 - 29 °C |
|
|
|
Weight increase (%) |
(Maximum) |
45 |
|
Thickness increase (%) |
(Maximum) |
10 |
6 |
After immersion in ASTM Fuel B for 22 Hrs. @ 21 - 29 °C |
|
|
|
Weight increase (%) |
(Maximum) |
40 |
|
Thickness increase (%) |
(Maximum) |
10 |
7 |
After immersion in Water for 22 Hrs. @ 21 - 29 °C |
|
|
|
Weight increase (%) |
(Maximum) |
55 |
|
Thickness increase (%) |
(Maximum) |
30 |
8 |
Dimensions |
|
|
(a) |
Thickness |
|
0.5 mm to 1.5 mm |
(b) |
Thickness Variations |
(1) 0.5mm - 0.9mm
(2) 1.0mm - 1.5mm |
(1) Rolls of 1200mm width
(2) In sheets of 1200mm X 1000mm |
(c) |
Thickness Tolerance |
|
0.25mm to 0.50mm--- +/- 0.08mm 0.60mm to 1.5mm--- +/- 0.13mm |
9 |
ASTM Specification Compliance |
|
ASTM F104 : 334156 M6 |